Nuclear Power Plant pump castings DPTesting/crack detection,Bangalore,India





Pump castings & shafts for Nuclear power plant assemblies were tested by Team Trinity NDT using Fluorescent penetrant inspection for crack detection / discontinuity detection at NDT facility in Bangalore, india.

Fluorescent penetrant Inspection FPI revealed fine pinholes both isolated and clustered at some important areas of castings (see adjacent photos with marked areas).'Team Trinity NDT' is equipped with state of art NDT equipment including Ultrasonic flaw detection, Magnetic crack detection, Dye liquid penetrant testing, Radiography, material testing facilities and trained, qualified, certified personnel to carryout most critical applications round the clock in Bangalore, Hyderabad,Visakhapatnam (Vizag), Chennai, Mumbai,Delhi and throughout India. Trinity NDT also conducts ASNT NDT Course trainings (Level 1, Level 2) in Bangalore, Mumbai, Hyderabad, Vizag and at customer's works in India and abroad.

Comments

  1. ennio curtoApril 13, 2010 at 2:29 AM

    NEW TECHNIQUE FOR RESIDUAL STRESS MEASUREMENT NDT


    This type of non-destructive method NDT provides the possibility to measure residual stress and the effect of the service load with an impact device and a vibration measurement sensor. Internal stresses are to be considered as the following: 1) Operational strains referring to loads that the material is subject and calculated 2) Residual stresses in the material caused by heat treatments or stresses caused by welding, forging, casting, etc. The new technique is able to measure the applied load and residual stress that are balanced on the surface of the material, and in a relatively large volume, at times even the same size as the entire structures. This stress is part of the metal’s elasticity field and has a three axis spatial orientation. The system works through the accelerometer mounted with a magnetic base to generate the acceleration value of the vibrations created by the device impacting on the metal surface.
    The acceleration value, in combination with other parameters, permits obtaining the exact value of the residual stress or load applied in the desired point. This value will appear on the display directly in N / mm ². For non-magnetic metals, wax or gel will be used to mount the accelerometer.
    This new system, for buildings, bridges steel inspection is very simple for to use , portable ,measure exact values of residual stress due to welding and the applied loads. After many years of research and tests, and between e discover about elastics behaviour in field of metal steel now is very practice inspection point to point building and bridge constructions. This new system let bridges steel inspection in very simple mode, is portable instrument and let to measure exact values of residual stress due to welding and the applied loads.

    p.i. Ennio Curto

    more info: www.scribd.com/doc/6067883/New-Technique-for-Residual-Stress-Measurement-NDT-

    ReplyDelete

Post a Comment

Ask, Comment, Suggest to Ravi at Trinity NDT's Blog

Popular posts from this blog

Internal Welding Defects - A Guide

Image
  Internal Welding Defects - A Guide  Contents: Common Types of Internal Welding Defects  Causes of Internal Welding Defects  Detection Methods  Impact on Structural Integrity  Industry Standards and Regulations  Advancements in Welding Technology  The Role of Skilled Welders Let us know Welding is a critical process in various industries, ensuring the structural integrity of assembled components. However, even in the hands of skilled welders, internal welding defects can compromise the quality of the welds, leading to potential hazards and failures.   Introduction  In the realm of welding, understanding internal defects is paramount to achieving durable and reliable welded joints.  This article delves into the intricate world of internal welding defects, shedding light on their types, causes, detection methods, and preventive measures.  Importance of Weld Quality  Weld quality is not just a matter of aesthetics; it’s a crucial factor in determining the longevity and reliabilit
Read more

NDT Job Vacancies in Mumbai, India for NDT Level II freshers

Image
NDT Job Vacancies in Mumbai, India for NDT Level II freshers 1)     APPLY   POST                                                       : NDT TRAINEES QUALIFICATION                                                : ANY degree and diploma holders LOCATION                                                           : Out of Mumbai VACANT                                                              : 35 nos SALARY DETAILS                                                : Minimum 6.5 to 7.5,                                                                                Free food and accommodation    2)APPLY POST                                                 : NDT MAINTANCE ENGINEERS QUALIFICATION                                                 : Diploma EEE and Degree EEE,ECE LOCATION                                                            : Mumbai VACANT                                                               : 10 Nos SALARY   DETAILS                   
Read more

What Causes Pinholes in Welding? Causes and Remedies - A Guide

Image
  What Causes Pinholes in Welding? Causes and Remedies - A Guide Contents Introduction  Understanding the Welding Process   Exploring the Causes of Pinholes  Impact of Pinholes on Weld Quality  Strategies for Prevention and Mitigation    Introduction   In the intricate world of welding, pinholes are a persistent challenge that welders encounter.  These tiny voids, often invisible to the naked eye, can significantly compromise the integrity and quality of a weld.  Understanding what pinholes are and why they need to be addressed is crucial for maintaining the structural integrity and functionality of welded components.  Definition of Pinholes in Welding   Pinholes in welding refer to small voids or discontinuities within the weld metal or at the weld interface.  These voids can vary in size, ranging from microscopic to more visible defects, depending on the welding process and parameters.  Pinholes are typically formed due to gas entrapment, contamination, or improper welding te
Read more